PC帝人L-1250Y

特性透明;中粘度;高流动应用领域工业部件;护理用品;机械部件;家用电器;劳保用品;照明灯具

物性性能测试条件测试方法测试结果单位密度
ASTM D792/ISO 11831.2
吸水率 23℃/24H
ASTM D570/ISO 620.2%物理性能测试条件测试方法测试结果单位透光率厚度3mmASTM D-100388%折射率
ASTM D-5421.585

厚度1.47mm (厚度3.05mm )UL 9494V-2
机械性能测试条件测试方法测试结果单位洛氏硬度
ASTM D-78577M标度拉伸率屈服点，-ASTM D-6386-断裂点，-ASTM D-638140-弯曲模量
ASTM D-7902230(22700)MPa(Kgf/cm拉伸强度屈服点，-ASTM D-63861(620)MPa(Kgf/cm断裂点，-ASTM D-63881(830)MPa(Kgf/cm拉伸模量
ASTM D-6382120(21600)MPa(Kgf/cm弯曲强度
ASTM D-79090(915)MPa(Kgf/cm压缩强度
ASTM D-69576(770)MPa(Kgf/cm耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-256140(14)j/m(kgf.cm/cm)艾氏、带缺口厚度3.2mmASTM D-256880(90)j/m(kgf.cm/cm)拉伸模量
ASTM D638/ISO 5272120(21600)kg/cm²(MPa)[Lb/in²]拉伸强度
ASTM D638/ISO 52761(620)屈服 81(830)断裂kg/cm²(MPa)[Lb/in²]伸长率
ASTM D638/ISO 5276%洛氏硬度
ASTM D785M-77
弯曲模量
ASTM D790/ISO 1782230(22700)kg/cm²(MPa)[Lb/in²]弯曲强度
ASTM D790/ISO 17890(915)kg/cm²(MPa)[Lb/in²]拉伸断裂伸长率(延伸率)
ASTM D638/ISO 527140%Charpy冲击强度
ASTM D256/ISO 179140(14)kg·cm/cm(J/M)ft·lb/in光学性能测试条件测试方法测试结果单位透光率
ASTM D1003/ISO 1346888%折射率
ASTM D542/ISO 4891.585
热性能测试条件测试方法测试结果单位线性膨胀系数
ASTM D696/ISO 113597X10^-5mm/mm.℃线膨胀系数流动方向(垂直方向)ASTM D-6967
负荷挠曲温度负荷0.451MPa(4.6kgf/cm)ASTM D-648143°C温度指数电学式，厚度1.47mmUL 746B125°C冲击式，厚度1.47mmUL 746B115°C非冲击式，厚度1.47mmUL 746B125°C负荷挠曲温度负荷1.813MPa(18.6kgf/cm)ASTM D-648143°C电气性能测试条件测试方法测试结果单位耐导电径迹性CTIIEC 112300V耐电弧性
ASTM D-495110secc介电正切60Hz(10ASTM D-1500.0004(0.009)
体积电阻率
ASTM D-2573
绝缘破坏强度快速加压值厚度1.6mmASTM D-14930KV/mm介电率60Hz(10ASTM D-1502.95(2.9)
耐电弧性
ASTM D495/IEC 60112110
体积电阻率
ASTM D257/IEC 600933Ω.cm加工性能测试条件测试方法测试结果单位收缩率流动方向(垂直方向)ASTM D-9550.5～0.7%基本性能测试条件测试方法测试结果单位吸水率24hr，in 23℃ASTM D-5700.20%